| 1. High Alumina Brick Description |
High alumina bricks are mainly made of clinker of bauxite and other materials, mixed at high temperature, formed, dried, and sintered. The Al2O3 content of high alumina bricks varies according to different ratios. The general content is stable at 48%-80%, the maximum alumina content can reach 90%, and the refractory temperature can reach 1770℃.
International code name |
SK35 |
SK36 |
SK37 |
SK38 |
SK40 |
Al2O3/% |
≥48 |
≥55 |
≥65 |
≥75 |
≥80 |
Fe2O3/% |
≤2 |
≤2 |
≤2 |
≤2 |
≤2 |
Refractoriness |
≥1750 °C |
≥1770 °C |
≥1790 °C |
≥1790 °C |
≥1790 °C |
Apparent porosity |
≤22% |
≤22% |
≤23% |
≤23% |
≤21% |
Cold crushing strength |
≥39Mpa |
≥44Mpa |
≥49Mpa |
≥54Mpa |
≥65Mpa |
Refractoriness under load (0.2MPa) |
≥1420 °C |
≥1470°C |
≥1500 °C |
≥1520 °C |
≥1530 °C |
Reheating Linear Change (1500°C 2h) % |
+0.1~ -0.4 |
+0.1~ -0.4 |
+0.1~ -0.4 |
+0.1~ |
+0.1~ -0.4 |
| 2. High Alumina Brick Features |
1. High strength.
2. Strong pressure resistance.
3. The content of iron and other impurities is extremely low.
4. Lightweight and energy-saving.
5. Low heat storage
6. Can be heated quickly
| 3.High Alumina Brick Application |
1. Iron & steel making industry: Blast furnace,hot blast stove,electric furnace,ladle,tundish,heating furnace,refining furnace,reheating furnace,annealing furnace,cupola furnace.
2. Non-ferrous Metal industry: Smelting furnace, refining furnace, reverberatory furnace, converter furnace.
3. Building materials industry: Cement kiln, glass kiln, ceramic kiln, lime kilns, kiln car, tunnel kiln.
4. Energy & Incineration: Coke oven, circulating fluidized bed boiler, carbon roasting furnace, incinerators.
Others: Petrochemical industry furnace.